Grain Direction In Sheet Metal Bending

In the example above perhaps were using a certain type of steel and specific bend radius whereby we need to be careful to ensure the sheet metal does not crack due to bending.

Grain direction in sheet metal bending.

This can drastically limit the length of parts being formed as most materials grain runs in the long direction but as stated previously reducing the material s grain size may be a solution to this. The grain direction of the metal also contributes to the amount of springback that occurs in a bending operation. In addition the grain direction needs to be considered when the bend radius is less than twice the thickness depending on the material and its hardness. This micrograin impacts the design in terms of strength and appearance.

When sheetmetal is bend perpendicular to rolling direction grain rearranges. Bending with the grain gives a different result than bending against it. The grain direction is in the rolling direction of the sheet as it was being manufactured. You can see it on a new piece of sheet metal by noticing the direction of visible lines running through it.

Whereas bending parallel to rolling direction can lead to cracks because of destruction in grain structure. Bending metal against the grain or perpendicular to the grain is a common way to prevent material failure or cracking. The grain direction is established during the metal rolling process. The grain direction created in the direction the sheet is rolled at the mill runs the length of the full sheet.

Bending with the grain or parallel to the grain direction can be a contributor to material failure as bending along the grain allows for separation of the grain boundaries. The raw sheet has a natural micrograin direction that runs parallel to the 144 in. We can manually control the grain direction of the metal in the flat pattern and subsequently how the bounding box is oriented to address these concerns. Applying this to metal bending be it plate bending press braking or any other type of metal forming consideration must be given to the grain direction before any process is carried out.

Two rollers compressing the hot metal cause the polycrystalline material to elongate in the direction of rolling. A metal s grain direction is usually only a factor when bending however. During sheet metal processing rolling operation material grains are arranged in the direction of rolling. This occurs because bending along the grain allows for separation of the grain boundaries.

This is because sharper or tighter bends can be made across the grain without cracking. Once the crystallites are elongated they appear as the grain that we see in cold rolled steel. Bends that run perpendicular to the material s natural grain require slightly more pressure than those running parallel to the grain. When the sheet is made its particles become elongated in the direction of rolling.

That has negligible impact on part strength.